Glassceramics based on mill tailings of lead-zink ores

M. V. PAVLOV ¹ , I. V. PAVLOV ¹ , A. V. LINEYTSEV ² , Dr. Sciences V. F. PAVLOV ³ ( e-mail: This email address is being protected from spambots. You need JavaScript enabled to view it. ) ; ¹ Special design and technological bureau? SCIENCE? KSC SB RAS (Russia, Krasno-yarsk)
² Institute of Non-Ferrous Metals and Materials Science Siberian Federal University (Russia, Krasnoyarsk)
³ Krasnoyarsk Scientific Center SB RAS (Russia, Krasnoyarsk)

Glass-ceramic material was obtained from the "tailings" of concentration of lead-zinc ores. The strength of the control samples was 22.26 MPa in bending and 90.22 MPa in compression. After 100 cycles of testing samples for frost resistance, the characteristics changed to values ??equal to 9.61 MPa in bending and 35.30 MPa in compression.