The study of the ZnO–SnO2 system was carried out, in particular, the possibilities of the synthesis of zinc orthostannate were considered. The temperature of the synthesis of a compound from simple oxides by solid-phase synthesis has been established. Obtained ceramics based on zinc orthostannate with additives 5; 7.5; 10 mol. % NiO and 5; 7.5; 10 mol. % MnO. The properties of the powders were studied using XRD, SEM, and BET. The synthesis temperature of dense ceramics was 1450 °C
I. I. Aksyutin, V. V. Anisimov, D. A. Antonov, M. A. Tarasenko, N. A. Makarov (D. I. Mendeleev Uni-versity of Chemical Technology of Russia, Moscow, Russia)
1. Myung-Jin Kim, Seong-Hun Park, Young-Duk Huh. Photocatalytic Activities of Hydrothermally Synthesized Zn2SnO4 // Bull. Korean Chem. Soc. 2011. V. 32, No. 5. P. 1757.
2. Chandrappa K. Govindappa, Venkatesha T. Venkatarangaiah, Sharifah B. Abd Hamid. Electro-chemical Generation of Cubic Shaped Nano Zn2SnO4 Photocatalysts // Nano-Micro Lett. 2013. V. 5, Is. 2. P. 101 – 110.
3. Сидорак А. В., Шубин А. А., Иванов В. В., Нико-лаева Н. С. Синтез порошков Zn2SnO4 термообра-боткой соосажденных соединений // Журн. Сибир-ского федерального университета. Химия. 2011. Т. 4, № 3. С. 285 – 293.
4. Николаева Н. С., Иванов В. В., Шубин А. А. Синтез высокодисперсных форм оксида цинка: химическое осаждение и термолиз // Журн. Сибирского феде-рального университета. Химия. 2010. Т. 2, № 3. С. 153 – 173.
5. Макаров Н. А. Использование добавок, образую-щих жидкую фазу при обжиге, в технологии корундовой керамики // Стекло и керамика. 2003. № 10. С. 31 – 34.
[Makarov N. A. Use of Additives Forming Liquid Phase in Firing in Corundum Ceramics Technology (A Review) // Glass Ceram. 2003. V. 60, No. 9–10. P. 334 – 338.]
The article can be purchased
electronic!
PDF format
500 руб
UDK 666.3:666.9-129
Article type:
Not-set
Make a request