A method has been developed for one-sided etching of the inlet openings of channels of non-etched blanks of microchannel plates in dilute hydrofluoric acid. Blanks of microchannel plates MCP 18-10 were used in the work. The treatment was carried out in 0.2 n. hydrofluoric acid solution at room temperature without oscillation and mixing of the solution.
The results obtained allow us to assert that the etching of the channel inlets is more than 10 % of the diameter of the MCP 18-10 channels, which increases the electronic transparency of the device.
Oleg G. Ashkhotov – Doctor of Physics and Mathematics, Professor, Department of Electronics and Digital Information Technology, Kabardino-Balkarian State University, Nalchik, Russia
Irina B. Ashkhotova – Candidate of Technical Sciences, Doсent, Department of Electronics and Digital Information Technology, Kabardino-Balkarian State University, Nalchik, Russia
Tamerlan T. Magkoev – Doctor of Physics and Mathematics, Professor, Department of Condensed Matter Physics, North Ossetian State University, Vladikavkaz, Russia
1. Николаев Д. Н. Электронно-оптические преобразователи. История развития и виды поколений // Доклады ТУСУРа. 2007. № 1(15). С. 29 – 33.
2. Кулов С. К. Качество поверхности микроканальных пластин. Ч. 3. Химические свойства поверхности силикатных стекол. Владикавказ: Изд-во «Терек» СКГТУ, 2002. 336 с.
3. Бекузаров Т. В., Алкацева Т. Д., Самканашвили Д. Г., Кривов С. В. Исследование поверхностного слоя НВЗ на различных стадиях механической обработки // XXXVI Международная научно-практическая конференция «Приоритеты мировой науки: Новые подходы и актуальные исследования»: сб. тр. 30 декабря 2022 г. Анапа. Анапа, 2022. 137 с.
4. Ашхотов О. Г., Ашхотова И. Б., Магкоев Т. Т. Взаимодействие свинцовосиликатных стекол с разбавленными растворами фтористоводородной кислоты // Стекло и керамика. 2021. № 5. С. 40 – 43. [Ashkhotov O. G., Ashkhotova I. B., Magkoev T. T. Interaction of lead-silicate glasses with dilute solutions of fluoric acid Ashkhotov O. G., Ashkhotova I. B., Magkoev T. T. Interaction of lead-silicate glasses with dilute solutions of fluoric acid // Glass Ceram. 2021. V. 78, No. 5–6. P. 204 – 206.]
5. Ашхотова И. Б. Влияние физико-химических операций на процесс формирования исполнительной поверхности микроканальных пластин: дис. … канд. техн. наук. Владикавказ: СКГТУ, 2003. 122 с.
6. Молчанов В. С., Андрианова Л. В. Скорость разрушения оптических стекол в растворах фтористоводородной кислоты // ОМП. 1973. № 11. С. 40.
7. Молчанова О. С., Орлова Л. А., Красиков С. Е. О взаимодействии пористого стекла со щелочью и плавиковой кислотой // Физ. и хим. стекла. 1989. Т. 4, № 2. С. 451 – 458.
8. Толмачев В. А., Окатов М. А., Пальчевский В. В. и др. Взаимодействие свинцовосиликатного стекла с разбавленными растворами плавиковой кислоты // Физ. и хим. стекла. 1990. Т. 16, № 1. С. 107 – 110.
9. Ашхотова И. Б., Ашхотов О. Г., Мусаева Э. Б. Химическая устойчивость НВЗ МКП в разбавленных растворах плавиковой кислоты // Тезисы докладов региональной конференции «Вакуумная электроника на Северном Кавказе». 24 – 29 сентября 2002. г. Нальчик. Нальчик: Изд-во КБГУ, 2002. 89 с.
The article can be purchased
electronic!
PDF format
500
DOI: 10.14489/glc.2024.08.pp.007-010
Article type:
Research Article
Make a request